Quantification of hydrogen trapping in multiphase steels : Part I – Point traps in martensite

Turk, A. and Joshi, G.R. and Gintalas, M. and Callisti, M. and Rivera-Díaz-del-Castillo, P.E.J. and Galindo-Nava, E.I. (2020) Quantification of hydrogen trapping in multiphase steels : Part I – Point traps in martensite. Acta Materialia, 194. pp. 118-133. ISSN 1359-6454

Full text not available from this repository.

Abstract

We quantified systematically the H trap density in martensite resulting from the presence of dislocations, grain boundaries and retained austenite through a combination of detailed microstructural characterisation, H permeation, thermal desorption and diffusion modelling. This thorough analysis allowed for the first time to deconvolve key microstructural constituents affecting H diffusion in multi-trap martensite. Three microstructures were investigated – as-quenched, tempered at 300 °C and tempered at 450 °C. The first two microstructures had identical dislocation densities and grain size, while the as-quenched one also contained 3.5 vol.% of retained austenite. The two tempered microstructures showed a large difference in dislocation density with few other microstructural differences. The as-quenched microstructure exhibited over an order of magnitude lower H diffusivity and increased H trapping due to retained austenite, while the tempered samples exhibited very similar diffusivities, indicating that dislocations have a limited effect on H trapping. Trap density scaling laws were successfully identified and validated through diffusion simulations and experiments. It was also shown that in martensite and heavily deformed ferrite, where the average grain size is small, grain boundaries are more effective trapping sites than dislocations. Our results also show that retained austenite cannot be effectively modelled as a point trap under the local equilibrium assumption, which is frequently used to model its effect on H diffusion, and that bulk trapping must be considered at least in two dimensions, which is addressed in part II of this series. © 2020 Acta Materialia Inc.

Item Type:
Journal Article
Journal or Publication Title:
Acta Materialia
Uncontrolled Keywords:
/dk/atira/pure/subjectarea/asjc/2500/2507
Subjects:
?? austenitedislocation densitygrain boundarieshydrogen diffusionthermal desorption analysis (tda)advanced high strength steeldiffusiongrain size and shapehydrogenmicrostructureas-quenched microstructureaverage grain sizedislocation densitieshydrogen trappin ??
ID Code:
144511
Deposited By:
Deposited On:
04 Jun 2020 16:05
Refereed?:
Yes
Published?:
Published
Last Modified:
15 Jul 2024 20:41