Time-Resolved in Situ Synchrotron X-ray Diffraction Studies of Type 1 Silicon Clathrate Formation

Hutchins, Peter T. and Leynaud, Olivier and O'Dell, Luke A. and Smith, Mark E. and Barnes, Paul and McMillan, Paul F. (2011) Time-Resolved in Situ Synchrotron X-ray Diffraction Studies of Type 1 Silicon Clathrate Formation. Chemistry of Materials, 23 (23). pp. 5160-5167. ISSN 0897-4756

Full text not available from this repository.

Abstract

Silicon clathrates are unusual open-framework solids formed by tetrahedrally bonded silicon that show remarkable electronic and thermal properties. The type I structure has a primitive cubic unit cell containing cages occupied by metal atoms to give compositions such as Na8Si46 and Na2Ba6Si46. Although their structure and properties are well described, there is little understanding of the formation mechanism. Na8Si46 is typically produced by metastable thermal decomposition under vacuum conditions from NaSi, itself an unusual structure containing Si44– polyanions. In this study, we used in situ synchrotron X-ray diffraction combined with rapid X-ray detection on samples taken through a controlled temperature ramp (25–500 °C at 8 °C/min) under vacuum conditions (10–4 bar) to study the clathrate formation reaction. We also carried out complementary in situ high-temperature solid-state 23Na NMR experiments using a sealed tube loaded under inert-gas-atmosphere conditions. We find no evidence for an intermediate amorphous phase during clathrate formation. Instead, we observe an unexpectedly high degree of structural coherency between the Na8Si46 clathrate and its NaSi precursor, evidenced by a smooth passage of several X-ray reflections from one structure into the other. The results indicate the possibility of an unusual, epitaxial-like, growth of the clathrate phase as Na atoms are removed from the NaSi precursor into the vacuum.

Item Type: Journal Article
Journal or Publication Title: Chemistry of Materials
Uncontrolled Keywords: /dk/atira/pure/subjectarea/asjc/1600
Subjects:
Departments: VC's Office
ID Code: 65028
Deposited By: ep_importer_pure
Deposited On: 06 Jun 2013 12:33
Refereed?: Yes
Published?: Published
Last Modified: 30 Sep 2019 17:31
URI: https://eprints.lancs.ac.uk/id/eprint/65028

Actions (login required)

View Item View Item