Tungsten bronze-based nuclear waste form ceramics. Part 2: Conversion of granular microporous tungstate-polyacrylonitrile (PAN) composite adsorbents to leach resistant ceramics

Griffith, Christopher S. and Sebesta, Ferdinand and Hanna, John V. and Yee, Patrick and Drabarek, Elizabeth and Smith, Mark E. and Luca, Vittorio (2006) Tungsten bronze-based nuclear waste form ceramics. Part 2: Conversion of granular microporous tungstate-polyacrylonitrile (PAN) composite adsorbents to leach resistant ceramics. Journal of Nuclear Materials, 358 (2-3). pp. 151-163.

Full text not available from this repository.

Abstract

Conversion of a granular molybdenum-doped, hexagonal tungsten bronze (MoW-HTB)-polyacrylonitrile (PAN) composite adsorbent to a leach resistant ceramic waste form capable of immobilizing adsorbed Cs+ and Sr2+ has been achieved by heating in air at temperatures in the range 600-1200 degrees C. Thermal treatment of the Cs- and Sr-loaded composite material at 1000 degrees C was sufficient to invoke a 60% reduction in volume of the composite while still retaining its spherical morphology. Cs-133 MAS NMR studies of this sample suite at 9.4 T and 14.1 T showed that multiple Cs sites are present throughout the entire thermal treatment range. Scanning electron microscopy investigations of the phase assemblages resulting from thermal treatment demonstrated that the full complement of Cs, and the majority of Sr, partitions into HTB phases (A(0.16-0.3)MO(3); A = Cs+, Sr2+ and Na+; M = Mo, W). The potentially reducing conditions resulting from the removal of the PAN matrix or the presence of high concentrations of Na+ relative to either Cs+ or Sr2+ does not retard the formation of the high temperature HTB phases. The fraction of Cs+ and Sr2+ leached from the tungstate phase assemblages was superior or comparable with cesium hollandite (Cs0.8Ba0.4Ti8O18; f = approximate to 8 x 10(-5); rate = <1.2 x 10(-4) g/m(2)/day) and strontium titanate (SrTiO3; f = 3.1 x 10(-3); rate = 2.63 x 10(-4) g/m(2)/day), respectively, using a modified PCT test in Millipore water at 90 degrees C. Furthermore, where aggressive leaching conditions were employed (0.1 M HNO3; 150 degrees C; 4 days), the tungstate phase assemblages displayed leach resistance almost two orders of magnitude greater than the reference phases.

Item Type:
Journal Article
Journal or Publication Title:
Journal of Nuclear Materials
Uncontrolled Keywords:
/dk/atira/pure/core/keywords/physics
Subjects:
?? physicsgeneral materials sciencenuclear energy and engineeringnuclear and high energy physicsmaterials science(all)qc physics ??
Departments:
ID Code:
52880
Deposited By:
Deposited On:
24 Feb 2012 16:15
Refereed?:
Yes
Published?:
Published
Last Modified:
16 Jul 2024 09:00