Electrical conductivity properties of porous SmBaCo2O5+d and SmBa0.5Sr0.5Co2O5+d layered perovskite oxide systems for solid oxide fuel cell

Song, Kyeong Eun and Schlegl, Harald and Kim, Chan Gyu and Baek, Ki Sang and Lim, Yu Ri and Nam, Jung Hyun and Kim, Hyun-Suk and Kim, Jung Hyun (2022) Electrical conductivity properties of porous SmBaCo2O5+d and SmBa0.5Sr0.5Co2O5+d layered perovskite oxide systems for solid oxide fuel cell. Ceramics International, 48 (19 Par). pp. 28649-28658. ISSN 0272-8842

[thumbnail of Revised manuscript (Final version)]
Text (Revised manuscript (Final version))
Revised_manuscript_Final_version_.pdf - Accepted Version
Available under License Creative Commons Attribution-NonCommercial-NoDerivs.

Download (947kB)

Abstract

In this study, the electrical conductivity characteristics of SmBaCo2O5+d (SBCO) and SmBa0.5Sr0.5Co2O5+d (SBSCO) were measured and analyzed by changing the characteristics of the microstructure from dense microstructure to porous microstructure for the cathode application in solid oxide fuel cells. SBCO and SBSCO comprised of the dense microstructure showed metal insulator transition (MIT) and metallic behavior, respectively. In SBCO, when the oxygen partial pressure is reduced, the conductivity value decreases, and the conductivity behavior changes to the behavior of a semiconductor. However, the electrical conductivity behavior of SBSCO did not change even when the oxygen partial pressure was decreased. The electrical conductivities of the porous cathodes were lower than those of the dense cathodes due to the discontinuous electric path, but all porous cathodes showed semiconductor behavior. The conductivity value decreases when the oxygen partial pressure decreases, but the general conductivity behavior of the samples with a porous microstructure does not change under N2 atmosphere. The porous cathode showed the highest electrical conductivity when Pt lines were led to the top of the cathode. In this case, a relatively high electrical conductivity was measured using the method of measuring multiple conductivities at different temperatures while decreasing the measurement temperature starting from a high temperature rather than the method of measuring while raising the temperature starting from a low temperature. In the dense cathode, higher electrical conductivities were measured when a low current was applied, but in the porous cathode, the same electrical conductivity values were measured regardless of the applied current values.

Item Type:
Journal Article
Journal or Publication Title:
Ceramics International
Additional Information:
This is the author’s version of a work that was accepted for publication in Ceramics International. Changes resulting from the publishing process, such as peer review, editing, corrections, structural formatting, and other quality control mechanisms may not be reflected in this document. Changes may have been made to this work since it was submitted for publication. A definitive version was subsequently published in Ceramins International, 48, 19 Part A, 2022 DOI: 10.1016/j.ceramint.2022.06.179
Uncontrolled Keywords:
/dk/atira/pure/subjectarea/asjc/2500/2505
Subjects:
?? cathodeelectrical conductivityporous microstructuredense microstructurematerials chemistrysurfaces, coatings and filmsceramics and compositesprocess chemistry and technologyelectronic, optical and magnetic materials ??
ID Code:
174503
Deposited By:
Deposited On:
15 Aug 2022 09:50
Refereed?:
Yes
Published?:
Published
Last Modified:
25 Mar 2024 00:39