Additively manufactured foamed polylactic acid for lightweight structures

Yousefi Kanani, Armin and Rennie, Allan and Rahim, Shayfull Zamree Bin Abd (2023) Additively manufactured foamed polylactic acid for lightweight structures. Rapid Prototyping Journal, 29 (1). pp. 50-66. ISSN 1355-2546

[thumbnail of Manuscript_final_v2]
Text (Manuscript_final_v2)
Manuscript_final_v2.pdf - Accepted Version
Available under License Creative Commons Attribution-NonCommercial.

Download (2MB)


Purpose – This study aims to make foamed polylactic acid (PLA) structures with different densities by varying deposition temperatures using the material extrusion (MEX) additive manufacturing process. Design/methodology/approach – The extrusion multiplier (EM) was calibrated for each deposition temperature to control foaming expansion. Material density was determined using extruded cubes with the optimal EM value for each deposition temperature. The influence of deposition temperature on the tensile, compression and flexure characteristics of the foamable filament was studied experimentally. Findings – The foaming expansion ratio, the consistency of the raster width and the raster gap significantly affect the surface roughness of the printed samples. Regardless of the loading conditions, the maximum stiffness and yield strength were achieved at a deposition temperature of 200°C when the PLA specimens had no foam. When the maximum foaming occurred (220°C deposition temperature), the stiffness and yield strength of the PLA specimens were significantly reduced. Practical implications – The obvious benefit of using foamed materials is that they are lighter and consume less material than bulky polymers. Injection or compression moulding is the most commonly used method for creating foamed products. However, these technologies require tooling to fabricate complicated parts, which may be costly and time-consuming. Conversely, the MEX process can produce extremely complex parts with less tooling expense, reduction in energy use and optimised material consumption. Originality/value – This study investigates the possibility of stiff, lightweight structures with low fractions of interconnected porosity using foamable filament.

Item Type:
Journal Article
Journal or Publication Title:
Rapid Prototyping Journal
Additional Information:
This article is (c) Emerald Group Publishing and permission has been granted for this version to appear here. Emerald does not grant permission for this article to be further copied/distributed or hosted elsewhere without the express permission from Emerald Group Publishing Limited.
Uncontrolled Keywords:
?? fused deposition modellingadditive manufacturingmaterial extrusionfoamable polylactic acid filamentlightweight composite beamporous structuresmechanical engineeringindustrial and manufacturing engineering ??
ID Code:
Deposited By:
Deposited On:
11 Jul 2022 10:15
Last Modified:
22 Nov 2023 00:50