Aragon Zulke, Alana and Hoster, Harry and Mercer, Michael and Burrell, Robert and Li, Yi and Nagarathinam, Mangayarkarasi (2021) High-energy NCA cells on idle:anode versus cathode driven side reactions. Batteries & Supercaps.

Full text not available from this repository.

Abstract

We report on the first year of calendar ageing of commercial high‐energy 21700 lithium‐ion cells, varying over eight state of charge (SoC) and three temperature values. Lithium‐nickel‐cobalt‐aluminium oxide (NCA) and graphite with silicon suboxide (Gr‐SiOx) form cathodes and anodes of those cells, respectively. Degradation is fastest for cells at 70–80 % SoC according to monthly electrochemical check‐up tests. Cells kept at 100 % SoC do not show the fastest capacity fade but develop internal short circuits for temperatures T≥40 °C. Degradation is slowest for cells stored close to 0 % SoC at all temperatures. Rates of capacity fade and their temperature dependencies are distinctly different for SoC values below and above 60 %, respectively. Differential voltage analyses, apparent activation energy analysis, and endpoint slippage tracking provide useful insights into the degradation mechanisms and the respective roles of anode and cathode potential. We discuss how reversible losses of lithium might play a role in alleviating the rate of irreversible losses on commercial cells.

Item Type:
Journal Article
Journal or Publication Title:
Batteries & Supercaps
Subjects:
ID Code:
152946
Deposited By:
Deposited On:
19 Mar 2021 10:55
Refereed?:
Yes
Published?:
Published
Last Modified:
09 Jun 2021 05:51