Effects of Lap Thickness and Joint Geometry on Failure of Pultruded Composite Single-Lap Bolted Tension Joints

Turvey, Geoffrey John and Assassa, Jonathan (2017) Effects of Lap Thickness and Joint Geometry on Failure of Pultruded Composite Single-Lap Bolted Tension Joints. In: Advanced Composites in Construction 2017, 2017-09-052017-09-07, University of Sheffield.

Full text not available from this repository.

Abstract

Two series of single-lap, single-bolt composite joints were tested to failure in tension. The principal difference between them was the lap thickness (T). The 36 first series joints had T = 3.2 mm and the 45 second series joints had T = 6.4 mm laps. The joint layouts were defined in terms of their end distance to hole diameter (E/D) and width to hole diameter (W/D) ratios. The former ranged from 1.5 to 4 and the latter from 3 to 5. The individual and mean joint test data, presented in graphical format, comprise ultimate loads, strengths, strains and efficiencies (the latter based on ultimate strength) for the range of E/D ratios and specific W/D ratios. For the larger E/D ratios the thicker lap joints have ultimate loads about twice those of their thinner counterparts, whereas their ultimate strengths are only about 20% higher. The ultimate strains exhibit rather less clear trends, though strains up to 18000 με are achieved with large E/D and W/D ratios. The thinner lap joints have higher efficiencies (up to 36%) and the dominant failure modes (net tension and shear out) were observed in both joint series for the same E/D and W/D ratios.

Item Type:
Contribution to Conference (Paper)
Journal or Publication Title:
Advanced Composites in Construction 2017
ID Code:
88501
Deposited By:
Deposited On:
31 Oct 2017 16:04
Refereed?:
No
Published?:
Published
Last Modified:
19 Sep 2023 03:46