Krier, A. and Stone, M. and Krier, S. E. (2007) Characterization of InAs0.91Sb0.09 for use in mid-infrared light-emitting diodes grown by liquid phase epitaxy from Sb-rich solution. . Semiconductor Science and Technology, 22 (6). pp. 624-628. ISSN 0268-1242Full text not available from this repository.
The liquid phase epitaxial growth of InAs0.91Sb0.09 lattice-matched onto GaSb is reported for use in the active region of a mid-infrared light-emitting diode. Epitaxy was carried out from Sb-rich solution using Gd gettering to purify the material. The photoluminescence and electroluminescence emission spectra were studied over the temperature range 4–300 K using different excitation intensities. Interpretation of the resulting spectra revealed the existence of two acceptor levels with activation energies of 8 meV and 16 meV. Room temperature electroluminescence at 4.2 µm was readily obtained from homo-junction p–i–n diodes fabricated from this material. The temperature dependence of the electroluminescence was studied and the decrease in the radiative recombination coefficient was found to be primarily responsible for the luminescence quenching.
|Journal or Publication Title:||Semiconductor Science and Technology|
|Subjects:||Q Science > QC Physics|
|Departments:||Faculty of Science and Technology > Physics|
|Deposited By:||Dr Susan E. Krier|
|Deposited On:||12 Mar 2008 11:48|
|Last Modified:||04 Nov 2015 02:33|
Actions (login required)